Pure Tantalum Sheet, Tantalum Plate on Sale

Basic Info

Model NO.	R05200 R05400 R05255 R05252 Ta1 Ta10W Ta2.5W
Characteristic	Stable Electrical Behavior, Low Weight, High Capacitance
Protection	Resistance to Corrosion, High Melting Point
Usage	Alloys, Electronics
Shape	Plate
Concentrate or Not	Non-concentrate
Grade	Ta1, Ta-2.5W, Ta-10W
Density	16.64G/Cm3
Melting Point	3017
Standard	ASTM B521
Delivery Time	20 Days
Transport Package	Polywood Case or as Per Needs.
Specification	customized
Trademark	MD
Origin	Luoyang
HS Code	1111
Production Capacity	30000kg

Product Description

Tantalum rod,Tantalum bar,Tantalum sheet,Tantalum wire,Tantalum tube
Tantalum series ProductGrade: R05200 R05400 R05255 R05252 Ta1 Ta10W Ta2.5W

Technical conditions: ASTM B708-05 (Tantalum and its alloy sheet)

GB14841-2008 (Tantalum and its alloy bars)

ASTM B521-98 (Tantalum and its alloy tubing)

Purity: 99.95%

1) Can process specifications

Sheet 0.1min X 680max X 3000max

Foil 0.05min X 300max X Coils

Bar 1.0min X 3000max

Wire Φ0.1 X Coils

Pipe Φ1.0X 0.2min X 1000 max

grade	chemical composition %, max
	Fe	Si	Ni	W	Mo	Ti	Nb	O	C	H	N	Ta
Ta1 Ta2	0.005 0.005	0.005 0.005	0.005 0.005	0.005 0.005	0.002 0.002	0.002 0.002	0.005 0.1	0.02 0.03	0.004 0.1	0.002 0.002	0.005 0.01	remain remain

Dimension Tolerance

diameter mm	dia tolerance, mm			length, mm	length tolerance, mm
	forging	drawing	machining
3.0-4.5 4.5-6.5 6.5-10 10-16 16-18 18-25 25-40 40-50 50-65	- ±0.15 ±0.15 ±0.15 ±0.15 - - - -	0.05 - - - - - - - -	- - - - - ±0.5 ±0.5 ±0.6 ±0.7	500-1500 500-1500 400-1500 30-1200 200-1500 - - - -	±2 ±2 ±2 ±2 ±2 ±2 ±2 ±2

Mechanical Property

tantalum bar ( dia 3.18mm~63.5mm )
grade	ultimate tensile strength, min,pound / inch2 ( MPa )	yield strength, min, pound / inch2 (MPa)	elongation, min, % 1 inch (25.4mm), gauge length
R05400 R05200 R05252 R05255 R05240	25000 (172) 40000 (276) 70000 (482) 40000 (276)	15000 (103) 28000 (193) 55000 (379) 28000 (193)	25 20 20 20